The safety philosophy upon which the Swedish Nuclear Power Inspectorate’s (SKI) supervisory and regulatory activities are based assume that multiple physical barriers will exist and that a plant-specific defence-in-depth approach will be implemented at each plant. The physical barriers are situated between the radioactive material and the plant personnel and surroundings. In the case of...
Innehållstyp: Publikationer -
2005:60 Research and Service Experience with Environmentally-Assisted Cracking in Carbon and Low-Alloy Steels in High-Temperature Water
In this report, the most relevant aspects of research and service experience with environmentally assisted cracking of carbon and low-alloy steels in high-temperature water are reviewed, with special emphasis on the primary pressure-boundary components of boiling water reactors. The main factors controlling the susceptibility to environmentally assisted cracking under light water reactor...
Innehållstyp: Publikationer -
2005:61 Review and Assessment of SCC Experiments with RPV Steels in Oskarshamn 2 and 3 (ABB Report SBR 99-020)
Although the extent of cracking was rather surprising for a bolt-loaded specimen, the average stress corrosion crack growth rate of 0.5 mm/year over the five-year testing period does not represent an immediate concern. The overwhelming part of crack growth can have occurred during a 20 day chloride transient during the third year of exposure because of a condenser leakage after an outage. The...