2017:05 Robust structural verification of pressurized nuclear components subjected to ratcheting, part two – stress-strain curves for cyclic elastoplastic analysis.
Background Pressurized components in nuclear applications that are subjected to cyclic loading may exhibit progressive deformation, so called structural ratcheting. If the component is made out of a material that are deformation hardening, it may also exhibit material ratcheting. The combined effects of structural- and material ratcheting are not taken into account in the methods and material...
Innehållstyp: Publikationer -
2017:22 Effect of weld repairs on residual stresses in nickel base dissimilar metal welds
Background The driving force for crack growth near welds in nuclear application piping may arise from weld residual stresses. Experience from nondestructive examination show that cracks in dissimilar metal welds are often found near weld repairs. The repair welding may affect the residual stresses through e.g. increased tensile stresses and increased plastic straining on the surfaces of the...
Innehållstyp: Publikationer -
2017:12 Computational assessment of LOCA simulation tests on high burnup fuel rods in Halden and Studsvik
Background Loss of Coolant Accidents (LOCA) are among the most demanding accidents that can happen in a Light Water Reactor (LWR). The lack of cooling and the drop in pressure impose large stresses on the nuclear fuel which would increase the risk of fuel rod damage and the subsequent release of active material. But LOCA is also an accident that the nuclear power plant is designed to...
Innehållstyp: Publikationer -
2017:32 COMRAD – Comprehensive investigation of the performance of computed and digital radiography
Background Within the industry, there has long been a need to replace the traditional X-ray film and its handling. These both for economic and environmental considerations. Both computed radiography and digital radiography offer many advantages over the traditional use of x-ray with film. However, the transition from film-based radiography requires in-depth knowledge of the relationship...
Innehållstyp: Publikationer -
2013:32 Upparbetning av utbränt kärnbränsle - En studie med fokus på exportkontroll
Rapporten beskriver principerna för upparbetning samt egenskaperna hos utbränt kärnbränsle där sammansättningen hos det i reaktorn bildade plutoniumet är av avgörande betydelse för kärnvapenframställning till skillnad från civil upparbetning. Rapporten går igenom ett antal upparbetningsmetoder, både äldre metoder samt nya,...
Innehållstyp: Publikationer -
2003:15 Produktion av tungt vatten - En analys ur exportkontrollsynpunkt
Lena Oliver, Katarina Wilhelmsen Totalförsvarets forskningsinstitut, FOI 172 90, Stockholm. September 2003 SKI Svenska...
Innehållstyp: Publikationer -
2013:09 An Application of the Functional Resonance Analysis Method (FRAM) to Risk Assessment of Organisational Change
The objective of this study was to demonstrate an alternative approach to risk assessment of organisational changes, based on the principles of resilience engineering. The approach in question was the Functional Resonance Analysis Method (FRAM). Whereas established approaches focus on risks coming from failure or malfunctioning of components, alone or in combination, resilience engineering...
Innehållstyp: Publikationer -
2012:03 The IAEA Integrated Regulatory Review Service Mission to Sweden in February 2012
The Swedish Government decided on January 22, 2009 to mandate the Swedish Radiation Safety Authority, SSM, to apply for an international review of the Author-ity and its areas of supervision, an ‘IRRS’ (Integrated Regulatory Review Service) carried out by the International Atomic Energy Agency (IAEA). On February 25, 2009, SSM made a formal request to the IAEA for an IRRS in Sweden. The time...
Innehållstyp: Publikationer -
2011:33 Mathematical modelling of ultrasonic testing of components with defects close to a non-planar surface
The report describes work that has been performed in order to model ultrasonic testing of components that contain a defect close to a non-planar surface. The studies have been performed in both 2D and 3D, and in 2D in both the anti-plane (SH) and the in-plane (P-SV). The results show that the presence of a non-planar back wall can reduce the detectability of defects close to the surface. The...
Innehållstyp: Publikationer -
2011:19 Experimental evaluation of influence from residual stresses on crack initiation and ductile crack growth at high primary loads
Cracked components are usually subjected to loads causing both primary and secondary stresses, e.g. welding components. Engineering assessment approaches, such as the ASME XI code and the R6 procedure, are commonly used to conduct integrity assessment of such components. There has been an ongoing debate how to treat secondary stresses using engineering assessment methods. The nature of these...
Innehållstyp: Publikationer