2009:33 Workshop on spent fuel performance, radionuclide chemistry and geosphere transport parameters, Lidingö 2008: Overview and evaluation of recent SKB procedures
The safety assessment for disposal of spent nuclear fuel canister in the Swedish bedrock should thoroughly address the time period after a containment failure. Such a failure could be expected as a result of corrosion damage or mechanical failure due to rock movement. This report mainly covers some issues connected to parameters used for radionuclide transport calculations in the areas of...
Innehållstyp: Publikationer -
2010:09 Copper Thermodynamics in the Repository Environment up to 130˚C
The mechanisms of copper corrosion for a KBS-3 repository for spent nuclear fuel need to be known with a high level of confidence. This is because the overall rate of copper canister corrosion (accounting for corroding species concentrations, geochemical conditions and the mass transport through surrounding barriers) provides an essential performance indicator in safety assessment. A...
Innehållstyp: Publikationer -
2010:33 Lineament interpretation Short review and methodology
This report concerns a study which was initially conducted for the Swedish Nuclear Power Inspectorate (SKI), which is now merged into the Swedish Radiation Safety Authority (SSM). The conclusions and viewpoints presented in the report are those of the author and do not necessarily coincide with those of the SSM. In the characterization of a site that may have potential for hosting a...
Innehållstyp: Publikationer -
2010:05 Discrete-Feature Model Implementation of SDM-Site Forsmark
SSM has been following the investigations of the two candidate sites for a repository for spent nuclear fuel that the Swedish Nuclear Fuel and Waste Management Company (SKB) have been undertaking. SKB has reported the results of the investigations as site descriptive models. These models will be used to underpin the safety analysis following the license application of the repository planned...
Innehållstyp: Publikationer -
2016:39 Recommended residual stress profiles for stainless steel pipe welds
Background The Swedish Radiation Safety Authority (SSM) and the Swedish nuclear power plant owners have financed Inspecta Technology in Sweden to analyze stainless steel pipe welds to obtain good estimations of weld residual stress (WRS) distributions. Detailed knowledge of the residual stress field in different types of welds is important since they can have substantial influence on...
Innehållstyp: Publikationer -
2011:06 Reliability Data Handbook for Piping Components in Nordic Nuclear Power Plants – R Book, Phase 2
The Nordic PSA Group (NPSAG) has undertaken to develop a piping reliability parameter handbook for use in risk-informed applications that involve the consideration of structural integrity of piping systems. The scope of the handbook is to establish high quality reliability parameters that account for the Nordic and worldwide service experience with safety-related and non-safety-related piping...
Innehållstyp: Publikationer -
2010:47 Utveckling av programpaket för analys av termisk utmattning
I ett tidigare NESC-projekt (Network for Evaluating Structural Components – Thermal Fatigue) togs fram en Europeisk procedur för hantering av termisk utmattning. Den tidigare myndigheten Statens kärnkraftinspektion (SKI) var en av projektets finansiärer. Proceduren innehåller bl.a. utvärdering av en modell för analys av högcykelutmattning vid turbulent termisk...
Innehållstyp: Publikationer -
2011:05 Overview and Evaluation of the NESC Projects for Fracture Assessments of Nuclear Components
The Network for Evaluation of Structural Components (NESC) was started in 1993 and since then six different projects have been carried out. A seventh NESC-project is still in progress. The overall objective of these projects has been to study the reliability of the entire process of structural integrity assessment within an international framework. The network is coordinated by the European...
Innehållstyp: Publikationer -
2013:01 Validation of Weld Residual Stress Modeling in the NRC International Round Robin Study
Weld residual stresses (WRS) have a large influence on the behavior of cracks growing under normal operation loads and on the leakage flow from a through-wall crack. Accurate prediction on weld residual stresses is important to make proper decisions when cracks in weld joints are detected. During the latest years, there has been a strong development in both analytical procedures to...
Innehållstyp: Publikationer -
2014:21 Effects of additives on uranium dioxide fuel behavior
This report will form a basis for the reviews that SSM does when the license holders applies for use of nuclear fuel with additives. The report is also intended as a reference to the models that Quantum Technologies AB has developed. The report and the models will be a valuable source of information for SSM and other parties when discussing the performance of doped fuel. Ali Massih SSM...
Innehållstyp: Publikationer